| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Heating Treatment | Intermediate Frequency Quenching |
| Harden Layer | 8-12mm |
| Hardness | HRC59-62 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | HRC59-62 After Hardening |
| Micro Hardness | HV1250-1400 |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | Hard Chrome 60-80μm |
| Steel Wall Thickness | ≥70mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | HRC59-62 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm, American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Width | 2300mm×360mm |
| Steel Wall Thickness | ≥70mm |
| Heating Treatment | Intermediate Frequency Quenching, 9-12mm Harden Layer |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Coating Thickness | 60-80μm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | HRC60-62 After Hardening |
| Harden Layer Depth | 8-12mm |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Width | 2500mm×Φ385/360mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Width | 2800mm×Φ385/560mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Width | 2500mm×Φ295/346mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Width | 2500mm×Φ295/346mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |