Material | 50CrMoA Precision Forging Alloy Steel |
---|---|
Coating | Tungsten Carbide |
Speed | 400m/min |
Lifetime | 60-100 Million Meters |
Hardness | HV1250-1400 |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | 60-80μm, American Praxair Super Hard 1342 Tungsten Cabide Powder |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Harden Layer Depth | 8-12mm |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
Coating Thickness | 60-80μm |
Width | 2100mm*360mm |
Heating Treatment | Intermediate Frequency Quenching |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
Size | 2400mm*408mm |
Micro Hardness | HV1250-1400 |
Heating Treatment | Intermediate Frequency Quenching |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | 60-80μm, American Praxair Super Hard 1342 Tungsten Cabide Powder |
Width | 1800mm×Φ320/340mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 60-80μm |
Width | 2500mm×380mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Harden Layer Depth | 8-12mm |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
Width | 2100mm×340mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
Width | 2600mm*408mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Harden Layer Depth | 8-12mm |