| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Coating Thickness | 60-80μm |
| Width | 1800mm*320mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
| Width | 2100mm×340mm |
| Heating Treatment | Composite Heating |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | Hard Chrome 60-80μm |
| Size | 1600mm×320mm |
| Steel Wall Thickness | ≥70mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | HRC60-62 After Hardening |
| Harden Layer Depth | 8-12mm |
| Material | 50CrMoA Precision Forging Alloy Steel |
|---|---|
| Coating | Tungsten Carbide |
| Speed | 400m/min |
| Lifetime | 60-100 Million Meters |
| Hardness | HV1250-1400 |
| Material | 50CrMoA Refined Forging Alloy Steel |
|---|---|
| Coating | Tungsten Carbide |
| Speed | 400m/min |
| Lifetime | 60-100 Million Meters |
| Hardness | HV1250-1400 |
| Tungsten Carbide Powder | American Praxair 1342 Super-hard 1342 Tungsten Carbide Powder |
|---|---|
| Workpiece Shape | Shafts |
| Coating | 0.05-0.1m |
| Plating Technology | HVOF |
| Plating Equipment | American Praxair JP8000 |