Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
Size | 2300mm×340/360mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | Hard Chrome |
Thickness | 0.06-0.08mm |
Heating Treatment | Intermediate Frequency Quenching |
Harden Layer | 8-12mm |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | HRC60-62 After Hardening |
Harden Layer Depth | 8-12mm |
Material | 50CrMoA Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | HRC60-62 After Hardening |
Harden Layer Depth | 8-12mm |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
Size | 1650mm*300mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
Width | 2500mm×Φ360/408mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | 60-80μm, American Praxair Super Hard 1342 Tungsten Cabide Powder |
Width | 2350mm×Φ325/405mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
Size | 1900mm×Φ325mm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Material | 50CrMo Precision Forged Alloy Steel |
---|---|
Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
Coating Thickness | 60-80μm |
Heating Treatment | Intermediate Frequency Quenching |
Hardness | >HRC58 After Hardening |
Coating | Hard Chrome 60-80μm |
---|---|
Hardness | HRC68 |
Warranty | 8 Million Meters |
Regrinding Times | 3-4 Times |
Flute Height | 1.5mm |