| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Coating Thickness | 60-80μm |
| Width | 1800mm*320mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Heating Treatment | Intermediate Frequency Quenching |
| Harden Layer | 8-12mm |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Coating Thickness | 60-80μm |
| Width | 1800mm*320mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
| Width | 2250mm*340mm |
| Heating Treatment | Composite Heating Method |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Carbide Powder |
| Coating Thickness | 60-80μm |
| Heating Treatment | Composite Heating |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Coating Thickness | 60-80μm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | HRC59-62 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Coating Thickness | 60-80μm |
| Width | 2300mm×Φ345/405mm |
| Heating Treatment | Composite Heating |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Coating Thickness | 60-80μm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm American Praxair Super Hard 1342 Tungsten Cabide Powder |
| Heating Treatment | Composite Heating Method |
| Hardness | >HRC58 After Hardening |
| Harden Layer Depth | 8-12mm |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | American Praxair Super Hard 1342 Tungsten Cabide Powder 0.06-0.08mm |
| Hardness | >HRC58 After Hardening |
| Micro Hardness | HV1250-1400 |
| Flute Type | C Flute 3.4mm |