| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm Hard Chrome |
| Width | 1450mm×325mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | Hard Chrome |
| Width | 1650mm X 315/325mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm Hard Chrome |
| Size | 1900mm×310mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | Hard Chrome 60-80μm |
| Steel Wall Thickness | ≥70mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 45# Steel |
|---|---|
| Steel Wall Thickness | ≥50mm |
| Coating | Hard Chrome 50-80μm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC55 After Hardening |
| Material | 45# Steel |
|---|---|
| Coating | Hard Chrome |
| Coating Thickness | 50-80μm |
| Steel Wall Thickness | ≥50mm |
| Regrinding Times | 3-4 Times |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | Hard Chrome 60-80μm |
| Size | 1900mm*320mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | 60-80μm Hard Chrome |
| Size | 1200mm*230mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | Hard Chrome |
| Coating Thickness | 60-80μm |
| Size | 1450mm*260mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Material | 50CrMo Precision Forged Alloy Steel |
|---|---|
| Coating | Hard Chrome 60-80μm |
| Size | 1650mm ×Φ280mm |
| Heating Treatment | Intermediate Frequency Quenching |
| Hardness | >HRC58 After Hardening |